BeltShield® CV

Rubber Belt Repair System

BeltShield® CV is a 100% solid elastomeric polyurea developed for composite rubber repair system with cross linking properties to ShieldPrime SP to complete our RBRS system and ensure maximum adhesion to rubber as well as other varying substrates. RBRS is a volatile free, odorless system applied with 1:1 mix ratio with plural component spray equipment.

Technical/Performance Data

Cured Film Properties	Test Method	Typical Value
VOC	Theoretical	0%
Solids Content	Theoretical	100%
Shore A Hardness	ASTM D2240	80-85
Elongation	ASTM D638	300-450%
Tensile Strength, MPa	ASTM D638	6MPa-9MPa
Elastic Modulus, MPa	ASTM D638	3.5MPa-9MPa
Tear Strength	ASTM D624	53-79 kN/m
Moisture Vapour Transmission	ASMT E-96	0.02 perm
Taber Abrasion, mg wt loss (1000g, 1000rev CS-17)	ASTM D4060	8-18
Gel Time	ASTM D1640	10-18 seconds
Tack Free	ASTM D1640	~3 minutes

Tested in accordance to EPA 9090A, LARR Approval (CA)

The value ranges stated in this Technical Data Sheet are based on system processing under laboratory conditions. Equipment configurations and/or field application conditions may produce variances
in final system values.

Limitations: BeltShield® CV should not be used for direct contact with extremely high or low pH attack. Composite systems are available. Consult ShieldCrete® Technical team to discuss your specific case.